International Standard
ISO 9588:2007
Metallic and other inorganic coatings — Post-coating treatments of iron or steel to reduce the risk of hydrogen embrittlement
Reference number
ISO 9588:2007
Edition 2
2007-12
International Standard
Read sample
ISO 9588:2007
45972
Published (Edition 2, 2007)
This standard was last reviewed and confirmed in 2016. Therefore this version remains current.

ISO 9588:2007

ISO 9588:2007
45972
Language
Format
CHF 42
Convert Swiss francs (CHF) to your currency

Abstract

ISO 9588:2007 specifies procedures for reducing susceptibility, or degree of susceptibility, to hydrogen embrittlement that can arise in surface finishing processes.

The heat-treatment procedures for iron or steel specified in ISO 9588:2007 have been shown to be effective in reducing the susceptibility to hydrogen embrittlement. These heat-treatment procedures are used after surface finishing, but prior to any secondary conversion-coating operation.

Stress-relief heat-treatment procedures applied after fabrication, but prior to surface finishing, are specified in ISO 9587.

ISO 9588:2007 does not apply to fasteners.

General information

  •  : Published
     : 2007-12
    : International Standard to be revised [90.92]
  •  : 2
     : 5
  • ISO/TC 107/SC 3
  • RSS updates

Next version under development

Draft International Standard
ISO/DIS 24251-1
Prevention of hydrogen assisted brittle fracture of high-strength steel components — Part 1: Fundamentals and measures
Reference number
ISO/DIS 24251-1
Edition 1
Draft
International Standard

ISO/DIS 24251-1

Prevention of hydrogen assisted brittle fracture of high-strength steel components

Part 1: Fundamentals and measures

ISO/DIS 24251-1

ISO/DIS 24251-1
78213
Language
Format
CHF 63
Convert Swiss francs (CHF) to your currency

Got a question?

Check out our FAQs

Customer care
+41 22 749 08 88

Opening hours:
Monday to Friday - 09:00-12:00, 14:00-17:00 (UTC+1)